PENGARUH BAHAN TAMBAHAN TEXAPON TERHADAP KUAT TEKAN BETON RINGAN

  • Nurjanah universitas islam blitar
Abstract views: 611 , PDF (Bahasa Indonesia) downloads: 1366
Keywords: Keywords: Lightweight Concrete, Texafo and Concrete Compressive Strength, Lis Ayu Widari, Fasdarsyah,Iva Debrina, Mart 2015, Jurusan Teknik Sipil, Universitas Malikussaleh, Pengaruh Penggunaan Abu Serbuk Kayu Terhadap Kuat Tekan Dan Daya Serap Air Pada Paving Block Hunggurami ,Elia, Dosen pada Jurusan Teknik Sipil, FST Undana, Wilhelmus Bunganaen, Dosen pada Jurusan Teknik Sipil, FST Undana, Richardo Yeskial Muskanan, Penamat dari Jurusan Teknik Sipil, FST Undana, 2014. Mustain, 2006 diakses di https://harpimandala.files.wordpress.com/2013/11/teknik-sipil_abu-layang.pdf, pada tanggal 30 oktober 2017 Eka Wahyudianto, B., Muhammad Ujianto, S. T., & Yenny Nurchasanah, S. T. (2016). Tinjauan Kuat Tekan dan Kuat Lentur Dinding Pasangan Batu Bata Dengan Perkuatan Diagonal Tulangan Baja (Doctoral dissertation, Universitas Muhammadiyah Surakarta). SUSANTO, H., Fepy, S., & Agustin, G. PENGARUH PENGGANTIAN SEBAGIAN SEMEN DENGAN ABU SEKAM PADI YANG DIAMBIL DARI TEMPAT BERBEDA TERHADAP KUAT TEKAN BETON (Doctoral dissertation, Universitas Bengkulu). Agususilo, D. (2007). Kuat lekat dan panjang penyaluran baja polos pada beton ringan dengan berbagai variasi kait (Doctoral dissertation, Universitas Sebelas Maret Surakarta). Anugraha, R. B., & Mustaza, S. (2010). Beton ringan dari campuran Styrofoam dan serbuk gergaji dengan semen Portland 250, 300 dan 350 kg/m3. Jurnal Aplikasi Teknik Sipil, 8(2), 57-66.

Abstract

Development in the field of construction is very rapid, including in the construction of housing, hospital offices and so on. Concrete as a building material has long been used and widely applied by the community because it has advantages - advantages over other structural materials which have good strength, fire resistance, resistance to weather changes, and are relatively easy in construction. This research was conducted to determine the effect of substitution with Texafone additives on concrete compressive strength. The method used in this study is to make lightweight concrete substitute for texafon additives by 0%, 10% and 30% of the weight of lightweight Concrete sand which has been cured during 7 days later it was tested to get the compressive strength of lightweight concrete. The results showed the value of 0% substitution strength at 7 days is 6.2 Mpa, while an additional 10% is 5.21 Mpa and an additional 30% is 4.51 Mpa.

References

Lis Ayu Widari, Fasdarsyah,Iva Debrina, Mart 2015, Jurusan Teknik Sipil, Universitas Malikussaleh, Pengaruh Penggunaan Abu Serbuk Kayu Terhadap Kuat Tekan Dan Daya Serap Air Pada Paving Block

Hunggurami ,Elia, Dosen pada Jurusan Teknik Sipil, FST Undana, Wilhelmus Bunganaen, Dosen pada Jurusan Teknik Sipil, FST Undana, Richardo Yeskial Muskanan, Penamat dari Jurusan Teknik Sipil, FST Undana, 2014.

Mustain, 2006 diakses di https://harpimandala.files.wordpress.com/2013/11/teknik-sipil_abu-layang.pdf, pada tanggal 30 oktober 2017

Eka Wahyudianto, B., Muhammad Ujianto, S. T., & Yenny Nurchasanah, S. T. (2016). Tinjauan Kuat Tekan dan Kuat Lentur Dinding Pasangan Batu Bata Dengan Perkuatan Diagonal Tulangan Baja (Doctoral dissertation, Universitas Muhammadiyah Surakarta). SUSANTO, H., Fepy, S., & Agustin, G. PENGARUH PENGGANTIAN SEBAGIAN SEMEN DENGAN ABU SEKAM PADI YANG DIAMBIL DARI TEMPAT BERBEDA TERHADAP KUAT TEKAN BETON (Doctoral dissertation, Universitas Bengkulu). Agususilo, D. (2007). Kuat lekat dan panjang penyaluran baja polos pada beton ringan dengan berbagai variasi kait (Doctoral dissertation, Universitas Sebelas Maret Surakarta). Anugraha, R. B., & Mustaza, S. (2010). Beton ringan dari campuran Styrofoam dan serbuk gergaji dengan semen Portland 250, 300 dan 350 kg/m3. Jurnal Aplikasi Teknik Sipil, 8(2), 57-66.

PlumX Metrics

Published
2019-03-28
How to Cite
Nurjanah. (2019). PENGARUH BAHAN TAMBAHAN TEXAPON TERHADAP KUAT TEKAN BETON RINGAN. Jurnal Qua Teknika, 9(1), 31-42. https://doi.org/10.35457/quateknika.v9i1.698
Section
Articles